A fast drying emulsion, exhibiting a very matt finish.
Formulated as a double sided emulsion.
Higher rub resistance than STD Matt Emulsion AL5039-40.
Low foaming so suitable for aggressive pumps and anilox systems.
Low odour suitable for food packaging.
TECHNICAL CHARACTERISTICS | ||
Viscosity (DIN 4 @ 20°C) | 35-50 Seconds | |
PH | 7.8-8.8 | |
Solids | 30-40% | |
Gloss (Sheen @ 60° on Gloss Art) | 5-20 | |
Drying Speed | Medium - Fast | |
Rub Resistance. Gloss Art paper Good quality carton board Standard carton board |
>750 rubs >750 rubs >750 rubs |
|
Slip Values | Medium | |
Heat Resistance | 140°C | |
APPLICATION CHARACTERISTICS | ||
Single/Double Sided | Double | |
Recommended Minimum back up time | 90 minutes | |
Minimum Substrate Grammage | 80 gsm | |
Glueable | Yes | |
Foil Blockable | Yes | |
UV Varnishable | Yes | |
Recommended film weight | 2-4gsm wet | |
GENERAL TECHNICAL DETAILS | ||
Z-INKS AQUATINGS 226 has been formulated to provide a streak free finish, whilst possessing suitable re-solubility characteristics making it recommended for double sided work and turn applications. Back up times will depend however on substrate type, ink film weight and press conditions, although it is recommended that printed material has been left to set for at least 90 minutes prior to re-working. Optimum drying conditions would include the use of hot air knives, and IR lamps. IR lamps should be kept to a minimum, with direct stack temperatures not falling below 27°C or rise above 34°C. For short runs, stack temperatures may not reach the optimum figures, and this must be considered if attempting to back up work rapidly. Light application of a middle grade spray powder is recommended. |
||
STORAGE AND HANDLING | ||
Waterbased emulsions should not be exposed to temperatures below 5°C or above 35°C. During cold months, it is recommended that containers are kept off of cold floors and stored on pallets. The Pulse Printing Products range of emulsions have a 12 month shelf life - if unopened and stored in the correct conditions. Manufacture date is available on the label. |
||
DISCLAIMER | ||
The information contained in this product data sheet is correct to the best of our knowledge at the date of issue. It is intended as a guide for the optimum use of the named product and is not intended as a warranty or as a specification. The information relates only to the product specified and may not be suitable for combinations with other materials or in processes other than those specifically described herein. |